Please use this identifier to cite or link to this item:
|Title:||Optimum glass formation at off-eutectic composition and its relation to skewed eutectic coupled zone in the La based La-Al-(Cu,Ni) pseudo ternary system||Authors:||Tan, H.
|Keywords:||Bulk metallic glass
|Issue Date:||3-Sep-2003||Citation:||Tan, H., Zhang, Y., Ma, D., Feng, Y.P., Li, Y. (2003-09-03). Optimum glass formation at off-eutectic composition and its relation to skewed eutectic coupled zone in the La based La-Al-(Cu,Ni) pseudo ternary system. Acta Materialia 51 (15) : 4551-4561. ScholarBank@NUS Repository. https://doi.org/10.1016/S1359-6454(03)00291-X||Abstract:||Glass formation and its relation to the dendritic and eutectic growth has been investigated for the La100-x[Al0.412(Cu,Ni)0.588]x (x=30-56.3) and La86-yAl14(Cu,Ni)y (y=16-29) alloy systems. The experimental results show that in the La-rich pseudo ternary La-Al-(Cu,Ni) system, optimum glass formation actually occurs at an off-eutectic composition. A nearly fully amorphous rod with 12 mm in diameter can be obtained at an off-eutectic composition near La62Al15.7(Cu,Ni)22.3, while only a 1.5 mm diameter rod can be obtained fully amorphous for the eutectic alloy La66Al14(Cu,Ni)20. A strong dependence of GFA on the composition is observed for these alloys. In addition, formation of a composite (i.e. αLa dendrite reinforced glass matrix) in 12 mm diameter cast rods is observed over a wide range of composition, including the eutectic composition. It has been found that the GFA does not correlate well with the extent of the undercooled liquid region (ΔTx) and is not even closely related to the reduced glass transition temperature (Trg). These unusual observations in glass formation and its relation to the skewed eutectic coupled zone have been explained in terms of the competition between the growth of crystalline phases (i.e. eutectic and dendritic phases) and the formation of the amorphous phase. © 2003 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.||Source Title:||Acta Materialia||URI:||http://scholarbank.nus.edu.sg/handle/10635/114366||ISSN:||13596454||DOI:||10.1016/S1359-6454(03)00291-X|
|Appears in Collections:||Staff Publications|
Show full item record
Files in This Item:
There are no files associated with this item.
checked on Aug 19, 2019
WEB OF SCIENCETM
checked on Jul 10, 2019
checked on Aug 16, 2019
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.