Please use this identifier to cite or link to this item: https://doi.org/10.1063/1.1367398
DC FieldValue
dc.titleEffect of radio-frequency bias voltage on the optical and structural properties of hydrogenated amorphous silicon carbide
dc.contributor.authorCui, J.
dc.contributor.authorRusli
dc.contributor.authorYoon, S.F.
dc.contributor.authorTeo, E.J.
dc.contributor.authorYu, M.B.
dc.contributor.authorChew, K.
dc.contributor.authorAhn, J.
dc.contributor.authorZhang, Q.
dc.contributor.authorOsipowicz, T.
dc.contributor.authorWatt, F.
dc.date.accessioned2014-10-16T09:22:15Z
dc.date.available2014-10-16T09:22:15Z
dc.date.issued2001-06
dc.identifier.citationCui, J., Rusli, Yoon, S.F., Teo, E.J., Yu, M.B., Chew, K., Ahn, J., Zhang, Q., Osipowicz, T., Watt, F. (2001-06). Effect of radio-frequency bias voltage on the optical and structural properties of hydrogenated amorphous silicon carbide. Journal of Applied Physics 89 (11 I) : 6153-6158. ScholarBank@NUS Repository. https://doi.org/10.1063/1.1367398
dc.identifier.issn00218979
dc.identifier.urihttp://scholarbank.nus.edu.sg/handle/10635/96335
dc.description.abstractHydrogenated amorphous silicon carbide (a-Si1-xCx:H) films have been deposited using the electron cyclotron resonance chemical vapor deposition process under varying negative rf-bias voltage at the substrate. The optical and structural properties of these films are characterized using Rutherford backscattering spectroscopy, transmittance/reflectance spectrophotometry, photothermal deflection spectroscopy, Fourier transform infrared absorption, Raman scattering, and room temperature photoluminescence (PL). These films deposited using a gas mixture of silane, methane, and hydrogen at a constant gas flow ratio showed a slight increase in the carbon fraction x, but very obvious structural transformation, at increasing rf induced bias voltage from -20 to -120 V. Near stoichiometric a-Si1-xCx: H films with a carbon fraction x of almost 0.5 are achieved at low bias voltage range from -20 to -60 V. Visible PL with relatively low efficiency can be observed from such films at room temperature. For larger bias voltages from -80 to -120 V, slightly C-rich U-Si1-xCx:H films (x>0.5) with larger optical gaps are obtained. These films have relatively higher PL efficiency, and the relative quantum efficiency was also found to depend strongly on the optical gap. Structurally, it was found that there is an increase in the hydrogen content and carbon sp2 bonding in the films at larger bias voltages. The latter leads to an increase in the disorder in the films. The linear relationship observed between the Urbach energy E0 and B factor in the Tauc equation suggests that the local defects related to microstructural disorder resulting from alloying with carbon dominate the overall defect structure of the films. Substrate biasing is noted to be crucial for the formation of Si-C bonds, as deduced from the Raman scattering results. © 2001 American Institute of Physics.
dc.description.urihttp://libproxy1.nus.edu.sg/login?url=http://dx.doi.org/10.1063/1.1367398
dc.sourceScopus
dc.typeArticle
dc.contributor.departmentPHYSICS
dc.description.doi10.1063/1.1367398
dc.description.sourcetitleJournal of Applied Physics
dc.description.volume89
dc.description.issue11 I
dc.description.page6153-6158
dc.description.codenJAPIA
dc.identifier.isiut000169149900043
Appears in Collections:Staff Publications

Show simple item record
Files in This Item:
There are no files associated with this item.

SCOPUSTM   
Citations

17
checked on May 13, 2022

WEB OF SCIENCETM
Citations

18
checked on May 13, 2022

Page view(s)

149
checked on May 12, 2022

Google ScholarTM

Check

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.