dc.titleAC magnetic-field-induced heating and physical properties of ferrite nanoparticles for a hyperthermia agent in medicine
dc.contributor.authorBae, S.
dc.contributor.authorLee, S.W.
dc.contributor.authorHirukawa, A.
dc.contributor.authorTakemura, Y.
dc.contributor.authorJo, Y.H.
dc.contributor.authorLee, S.G.
dc.identifier.citationBae, S., Lee, S.W., Hirukawa, A., Takemura, Y., Jo, Y.H., Lee, S.G. (2009-01). AC magnetic-field-induced heating and physical properties of ferrite nanoparticles for a hyperthermia agent in medicine. IEEE Transactions on Nanotechnology 8 (1) : 86-94. ScholarBank@NUS Repository.
dc.description.abstractAC magnetic-field-induced heating, cytotoxicity, and bio-related physical properties of two kinds of spinel ferrite nanoparticles, soft (NiFe 2O4) and hard (CoFe2O4), with different mean particle sizes were investigated in this paper to confirm the effectiveness for an in vivo magnetic nanoparticle hyperthermia agent in biomedicine. AC magnetically induced heating temperature of the nanoparticles measured both in a solid and an agar state at different applied magnetic fields and frequencies clarified that the maximum heating temperature of NiFe 2O4 nanoparticles is much higher than that of CoFe 2O4 nanoparticles. In addition, it was demonstrated that solid-state NiFe2O4 nanoparticles with 24.8 and 35 nm mean particle size exhibited a promisingly high heating temperature (21.5° C-45°C) for a hyperthermia agent in the physiologically tolerable range of the ac magnetic field with less than 50 kHz of applied frequency. According to the magnetic and physical analysis results, the superior ac magnetically induced heating performance of NiFe2O4 nanoparticles was primarily due to their higher magnetic susceptibility (permeability) that directly induces a larger magnetic minor hysteresis loop area at the low magnetic field. Cytotoxicity test results, quantitatively estimated by methylthiazol tetrazolium bromide test method, verified that uncoated NiFe 2O4, chitosan-coated NiFe2O4, and CoFe2O4 showed a noncytotoxicity, which is clinically suitable for a hyperthermia agent application. © 2006 IEEE.
dc.subjectAC magnetic-field-induced heating
dc.subjectFerrite nanoparticles
dc.subjectIn vivo hyperthermia agent
dc.subjectMagnetic susceptibility
dc.contributor.departmentELECTRICAL & COMPUTER ENGINEERING
dc.description.sourcetitleIEEE Transactions on Nanotechnology
Appears in Collections:Staff Publications

Show simple item record
Files in This Item:
There are no files associated with this item.

Google ScholarTM



Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.