|dc.title||Crater wear mechanisms of TiN coated high speed steel tools|
|dc.identifier.citation||Lim, C.Y.H.,Lim, S.C.,Lee, K.S. (2000). Crater wear mechanisms of TiN coated high speed steel tools. Surface Engineering 16 (3) : 253-256. ScholarBank@NUS Repository.|
|dc.description.abstract||This paper examines the crater wear characteristics of TiN coated high speed steel tool inserts during dry turning of steel workpieces over a wide range of machining conditions. Scanning electron microscopy shows that cracking and attrition of the TiN coating on the rake face result in coating loss soon after machining begins. The subsequent wear of the exposed high speed steel substrate occurs via attrition, diffusion, and high temperature shear. A wear mechanism map linking the observed crater wear mechanisms to machining conditions reveals that transitions from one dominant mechanism to another may be related to variations in measured tool wear rates.|
|dc.contributor.department||MECHANICAL & PRODUCTION ENGINEERING|
|Appears in Collections:||Staff Publications|
Show simple item record
Files in This Item:
There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.