dc.titleBulk hard magnetic alloys in Nd-Fe-B system prepared by casting and melt spinning
dc.contributor.authorKong, H.Z.
dc.contributor.authorDing, J.
dc.contributor.authorWang, L.
dc.contributor.authorLi, Y.
dc.date.accessioned2014-10-29T08:37:42Z
dc.date.available2014-10-29T08:37:42Z
dc.date.issued2001
dc.identifier.citationKong, H.Z.,Ding, J.,Wang, L.,Li, Y. (2001). Bulk hard magnetic alloys in Nd-Fe-B system prepared by casting and melt spinning. Materials Transactions 42 (4) : 674-677. ScholarBank@NUS Repository.
dc.identifier.issn13459678
dc.identifier.urihttp://scholarbank.nus.edu.sg/handle/10635/106972
dc.description.abstractCylindrical cast rods and melt-spun ribbons of Nd60Fe30B10 and two Nd67Fe26B7 and Nd10Fe73B17 eutectic alloys were prepared by copper mold casting and melt spinning. Coercivity of the as-cast Nd60Fe30B10 rod was 434 kA/m. Coercivity of the cast rod was increased to 1285.6 kA/m after annealing due to the formation of Nd2Fe14B phase. The as-cast eutectic Nd67Fe26B7 rod, which is partially amorphous, exhibited coercivity value identical to that of the alloy Nd60Fe30B10 (∼430 kA/m). On the other hand, eutectic Nd10Fe73B17 shows better glass forming ability, but lower coercivity (∼100 kA/m).
dc.sourceScopus
dc.subjectBulk amorphous
dc.subjectCasting
dc.subjectEutectic
dc.subjectHard magnetic
dc.subjectNeodymium-iron-boron alloys
dc.typeArticle
dc.contributor.departmentMATERIALS SCIENCE
dc.description.sourcetitleMaterials Transactions
dc.description.volume42
dc.description.issue4
dc.description.page674-677
dc.description.codenMTARC
dc.identifier.isiutNOT_IN_WOS
Appears in Collections:Staff Publications

Show simple item record
Files in This Item:
There are no files associated with this item.

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.