|Title:||Electrospun α-Fe2O3 nanostructures for supercapacitor applications|
|Citation:||Binitha, G., Soumya, M.S., Madhavan, A.A., Praveen, P., Balakrishnan, A., Subramanian, K.R.V., Reddy, M.V., Nair, S.V., Nair, A.S., Sivakumar, N. (2013-10-14). Electrospun α-Fe2O3 nanostructures for supercapacitor applications. Journal of Materials Chemistry A 1 (38) : 11698-11704. ScholarBank@NUS Repository. https://doi.org/10.1039/c3ta12352a|
|Abstract:||Herein, we report the facile synthesis of two α-Fe2O 3 nanostructures with different morphologies via an electrospinning technique using ferric acetyl acetonate as a precursor and polyvinyl acetate and polyvinyl pyrrolidone as the respective polymers. The as-electrospun metal oxide-polymer composite fibers were sintered at 500 °C to obtain two distinct nanostructures, denoted as nanograins and porous fibers throughout this manuscript. These crystalline nanostructures were characterized using powder X-ray diffraction (XRD), Raman spectroscopy, scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDAX) and transmission electron microscopy (TEM). The characterization results elucidated the predominance of hematite (α-Fe2O3) with particle sizes of 21 and 53 nm, for the respective nanostructures. Electrophoretic deposition was carried out in order to fabricate thin film electrodes, which were then subjected to electrochemical analysis. Electrochemical characterization revealed that both of the fabricated electrodes exhibited excellent performance in 1 M LiOH electrolyte with specific capacitance values of 256 and 102 F g-1 for the porous fiber and nanograin structures, respectively, at a scan rate of 1 mV s-1 and excellent capacitance retention, even after 3000 cycles, thus making them promising electrode materials for energy storage devices. © 2013 The Royal Society of Chemistry.|
|Source Title:||Journal of Materials Chemistry A|
|Appears in Collections:||Staff Publications|
Show full item record
Files in This Item:
There are no files associated with this item.
checked on Jul 14, 2018
WEB OF SCIENCETM
checked on Jul 4, 2018
checked on Mar 11, 2018
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.