|Title:||Glass formation in the ternary Zr-Zr2Cu-Zr2Ni system|
|Citation:||Yang, H., Wang, J.Q., Li, Y. (2006-06-01). Glass formation in the ternary Zr-Zr2Cu-Zr2Ni system. Journal of Non-Crystalline Solids 352 (8) : 832-836. ScholarBank@NUS Repository. https://doi.org/10.1016/j.jnoncrysol.2006.01.083|
|Abstract:||Glass formation and glass forming ability in the ternary Zr-Cu-Ni system were studied systematically. For Cu mold casting, the critical size for glass formation was found to be 1 mm in a relatively wide composition range of 56-64 at.% Zr, 16-26 at.% Cu and 16-24 at.% Ni. The phases competing with glass formation were found to be Zr, Zr2Cu and Zr2Ni. Despite the fact that Cu and Ni are completely miscible with each other, they cannot be regarded as simple substitution to each other in the case of glass formation in the Zr-Zr2Cu-Zr2Ni ternary eutectic system. © 2006.|
|Source Title:||Journal of Non-Crystalline Solids|
|Appears in Collections:||Staff Publications|
Show full item record
Files in This Item:
There are no files associated with this item.
checked on Jul 17, 2018
WEB OF SCIENCETM
checked on Jun 27, 2018
checked on Apr 20, 2018
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.