Title: Analysis of delamination in IC packages using a new variable-order singular boundary element
Authors: Tay, A.A.O. 
Lee, K.H. 
Lim, K.M. 
Issue Date: 1998
Source: Tay, A.A.O.,Lee, K.H.,Lim, K.M. (1998). Analysis of delamination in IC packages using a new variable-order singular boundary element. Proceedings - Electronic Components and Technology Conference : 936-943. ScholarBank@NUS Repository.
Abstract: Delamination of interfaces in IC packages gives rise to critical and mechanical failures such as popcorn cracking. Hence it is important to be able to analyze the mechanics of delamination from small interfacial defects which may exist at interfaces due to contamination or random factors. This paper describes the mechanics of interfacial delamination and the application of the boundary element method to analyzing delamination propagation at interfaces. Now, a crack tip at an interface between two materials has an order of singularity which is a function of the material properties. For an accurate analysis, a special variable-order singular boundary element has been developed and used. The effect of defect size and location along the pad-encapsulant interface on interfacial delamination has been studied. It was found that the energy release rate or stress intensity factor increases with defect size as well as proximity to the pad Corner. This implies that when a small delamination near a pad corner delaminates the crack tip nearer the pad corner will propagate first. The analysis also shown that this delamination, once started, will continue until the crack tip reaches the pad corner. If the variation of interface toughness as a function of mode mixity is known, the delamination propagation behaviour can be determined. Depending on the shape of the curve describing the variation of interface toughness with mode mixity, the delamination growth can either be stable, catastrophic or initial unstable followed by stable growth.
Source Title: Proceedings - Electronic Components and Technology Conference
URI: http://scholarbank.nus.edu.sg/handle/10635/74958
ISSN: 05695503
Appears in Collections:Staff Publications

Show full item record
Files in This Item:
There are no files associated with this item.

Page view(s)

14
checked on Feb 16, 2018

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.