| Title: | High coercivity in mechanically alloyed BaFe10Al2O19 | Authors: | Wang, S. Ding, J. Shi, Y. Chen, Y.J. |
Issue Date: | Sep-2000 | Citation: | Wang, S., Ding, J., Shi, Y., Chen, Y.J. (2000-09). High coercivity in mechanically alloyed BaFe10Al2O19. Journal of Magnetism and Magnetic Materials 219 (2) : 206-212. ScholarBank@NUS Repository. https://doi.org/10.1016/S0304-8853(00)00450-9 | Abstract: | Al-substituted Ba-ferrite in the form of BaFe10Al2O19 was prepared by mechanical alloying and subsequent heat treatment. Their structure and magnetic properties were investigated in comparison with Ba-ferrite without Al substitution. After annealing at 1100 °C, a coercivity as high as 9.3 kOe was measured, while the coercivity values of the Ba-ferrite samples without Al substitution with a similar particle size were observed in the range of 5-6 kOe. A significant reduction of saturation magnetization was observed as compared to pure barium ferrite. | Source Title: | Journal of Magnetism and Magnetic Materials | URI: | http://scholarbank.nus.edu.sg/handle/10635/107059 | ISSN: | 03048853 | DOI: | 10.1016/S0304-8853(00)00450-9 |
| Appears in Collections: | Staff Publications |
Show full item record
Files in This Item:
There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.