|Title:||Mechanical properties of alternating high-low sp3 content thick non-hydrogenated diamond-like amorphous carbon films||Authors:||Teo, E.H.T.
|Issue Date:||Oct-2007||Citation:||Teo, E.H.T., Chua, D.H.C., Tay, B.K. (2007-10). Mechanical properties of alternating high-low sp3 content thick non-hydrogenated diamond-like amorphous carbon films. Diamond and Related Materials 16 (10) : 1882-1886. ScholarBank@NUS Repository. https://doi.org/10.1016/j.diamond.2007.08.035||Abstract:||Thick non-hydrogenated DLC films (∼ 1μm), consisting of alternating sub-layers of high/low sp3 content, were deposited onto n++ Si substrates using the filtered cathodic vacuum arc method. These films were systematically studied to determine how the changes in composition of the sub-layers would affect the mechanical properties such as intrinsic stress, hardness, friction coefficient, wear rate and surface roughness. Variations of both the ratio of hard to soft layers (from 1:3 to 3:1) and thickness of individual layers (from 12.5nm to 75nm) were studied in detail. The stress of the film was sufficiently lowered (7.8GPa-2.4GPa) by the multilayer approach. The results indicated that although hardness has some correlations with the internal composition of the film, the reduced Young's modulus is largely not affected. Wear and frictional characterizations also showed that the multilayer was a good candidate for many mechanical applications. © 2007 Elsevier B.V. All rights reserved.||Source Title:||Diamond and Related Materials||URI:||http://scholarbank.nus.edu.sg/handle/10635/86525||ISSN:||09259635||DOI:||10.1016/j.diamond.2007.08.035|
|Appears in Collections:||Staff Publications|
Show full item record
Files in This Item:
There are no files associated with this item.
checked on Jun 17, 2021
WEB OF SCIENCETM
checked on Jun 9, 2021
checked on Jun 21, 2021
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.