Please use this identifier to cite or link to this item: https://scholarbank.nus.edu.sg/handle/10635/58529
DC FieldValue
dc.titleNickel base wide gap brazing with preplacement technique Part 2 - Formation mechanisms of macrovoids
dc.contributor.authorLim, L.C.
dc.contributor.authorLee, W.Y.
dc.contributor.authorLai, M.O.
dc.date.accessioned2014-06-17T05:15:33Z
dc.date.available2014-06-17T05:15:33Z
dc.date.issued1995-10
dc.identifier.citationLim, L.C.,Lee, W.Y.,Lai, M.O. (1995-10). Nickel base wide gap brazing with preplacement technique Part 2 - Formation mechanisms of macrovoids. Materials Science and Technology 11 (10) : 1041-1045. ScholarBank@NUS Repository.
dc.identifier.issn02670836
dc.identifier.urihttp://scholarbank.nus.edu.sg/handle/10635/58529
dc.description.abstractMicrostructural inhomogeneities and variations in the extent of erosion of base metal in nickel base wide gap brazed joints produced by the preplacement technique with braze mixes of different gap filler contents were investigated, from which the flow behaviour of the braze mix constituents and the formation mechanisms of the various types of macrovoid were deduced. The results show that the formation of various types of macrovoid is closely related to the flow behaviour of the constituents of braze mixes during brazing, the latter in turn being strongly influenced by the braze mix ingredients, the brazing temperature, and the gap depth. For a wide gap brazed joint to be free from macrovoids, the braze mix must be sufficiently viscous to bridge the gap faying surfaces and must flow as a whole into the gap. Braze mixes with gap filler contents of 30-40% are ideal for such requirements. With too low a gap filler content, the molten filler would flow preferentially ahead of the mass of braze mix, leading to the formation of irregularly shaped macrovoids at the tail end of the joint. With too high a gap filler content, the molten filler metal available was insufficient to completely fill the interstices among the gap filler particles, leading to near spherical macrovoids in the braze mix deposit and adjacent joint area. At too low a brazing temperature, the braze mix would be too viscous to penetrate into the gap freely and local premature solidification would occur, leading to large, irregularly shaped macrovoids throughout the longitudinal section of the joint. © 1995 The Institute of Materials.
dc.sourceScopus
dc.typeArticle
dc.contributor.departmentMECHANICAL & PRODUCTION ENGINEERING
dc.description.sourcetitleMaterials Science and Technology
dc.description.volume11
dc.description.issue10
dc.description.page1041-1045
dc.description.codenMSCTE
dc.identifier.isiutNOT_IN_WOS
Appears in Collections:Staff Publications

Show simple item record
Files in This Item:
There are no files associated with this item.

Page view(s)

49
checked on Mar 21, 2020

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.