dc.titleStructure and magnetic characterization of amorphous and crystalline Nd-Fe-Al alloys
dc.contributor.authorWang, X.Z.
dc.contributor.authorLi, Y.
dc.contributor.authorDing, J.
dc.contributor.authorSi, L.
dc.contributor.authorKong, H.Z.
dc.date.accessioned2014-10-29T08:41:00Z
dc.date.available2014-10-29T08:41:00Z
dc.date.issued1999
dc.identifier.citationWang, X.Z.,Li, Y.,Ding, J.,Si, L.,Kong, H.Z. (1999). Structure and magnetic characterization of amorphous and crystalline Nd-Fe-Al alloys. Journal of Alloys and Compounds 290 (1-2) : 209-215. ScholarBank@NUS Repository.
dc.identifier.issn09258388
dc.identifier.urihttp://scholarbank.nus.edu.sg/handle/10635/107207
dc.description.abstractGlass formation has been studied in Nd60Fe30Al10 alloy produced by melt-spinning, water quenching and copper mold chill casting. Partially amorphous alloys were obtained by melt-spinning at low wheel speeds of 5 to 15 m/s and by water quenching of a 1-mm diameter rod, while fully amorphous alloys were obtained by melt-spinning at higher wheel speeds of 20 and 30 m/s and chill casting of a 1-mm diameter rod. A high coercivity was observed in the partially amorphous ribbon melt-spun at 5 m/s and water quenched rod, and in the fully amorphous chill cast rod, while low values of coercivity were obtained in fully amorphous ribbons melt-spun at high speeds of 20 and 30 m/s. Crystallization of water quenched and chill cast samples after heat treatment at high temperature resulted in a substantial reduction of the high coercivity. Results of X-ray diffraction indicate that formation of Nd and a ternary Fe-Nd-Al phase with an unknown crystal structure were present after crystallization. TEM results and a magnetic study of the heat treated samples indicate that as long as there is an amorphous phase produced by low cooling rate, the high coercivity remains. The high coercivity of bulk amorphous samples is discussed. The unknown ternary Fe-Nd-Al phase is antiferromagnetic with a Neel temperature at about 260 K. © 1999 Elsevier Science S.A. All rights reserved.
dc.sourceScopus
dc.typeArticle
dc.contributor.departmentMATERIALS SCIENCE
dc.description.sourcetitleJournal of Alloys and Compounds
dc.description.volume290
dc.description.issue1-2
dc.description.page209-215
dc.description.codenJALCE
dc.identifier.isiutNOT_IN_WOS
Appears in Collections:Staff Publications

Show simple item record
Files in This Item:
There are no files associated with this item.

Page view(s)

92
checked on Feb 22, 2020

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.