|Title:||Effect of boron addition to the hard magnetic bulk Nd60Fe30Al10 amorphous alloy||Authors:||Kong, H.Z.
|Issue Date:||Jul-2000||Citation:||Kong, H.Z., Li, Y., Ding, J. (2000-07). Effect of boron addition to the hard magnetic bulk Nd60Fe30Al10 amorphous alloy. Journal of Magnetism and Magnetic Materials 217 (1) : 65-73. ScholarBank@NUS Repository. https://doi.org/10.1016/S0304-8853(00)00343-7||Abstract:||A detailed study of the effect of boron addition to crystallinity, magnetic properties and thermal properties was carried out for alloys Nd60-xFe30Al10Bx with x = 0, 1, 3 and 5 produced by copper mold chill casting and melt-spinning. The cast rods of alloys Nd60-xFe30Al10Bx were largely amorphous. Remanence up to 0.154 T and coercivity up to 355 kA/m were observed, which were higher than those of the bulk amorphous Nd60Fe30Al10 rod of the same diameter. A step in hysteresis loop was observed for the hard magnetic cast rod and ribbon melt-spun at a low speed of 5 m/s of the alloys with boron addition. Consistent increase in the amplitude of the step and magnetic field (H) at which the step was observed as the boron content increased. A single magnetic phase with low coercivity was observed for fully amorphous ribbon melt-spun at high speed of 30 m/s. Full crystallization due to heat treatment resulted in transition of hard magnetic amorphous phase of Nd55Fe30Al10B5 cast rod to paramagnetic crystalline phases. TEM results of the as-cast rods illustrated the existence of numerous minute Nd-crystallites in amorphous matrix.||Source Title:||Journal of Magnetism and Magnetic Materials||URI:||http://scholarbank.nus.edu.sg/handle/10635/107011||ISSN:||03048853||DOI:||10.1016/S0304-8853(00)00343-7|
|Appears in Collections:||Staff Publications|
Show full item record
Files in This Item:
There are no files associated with this item.
checked on Nov 27, 2020
WEB OF SCIENCETM
checked on Nov 19, 2020
checked on Nov 21, 2020
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.