dc.titleAnalysis of triple Co alloy layer magnetic thin films with different bias configuration
dc.contributor.authorJin, D.
dc.contributor.authorWang, J.P.
dc.contributor.authorGong, H.
dc.identifier.citationJin, D.,Wang, J.P.,Gong, H. (2000-09). Analysis of triple Co alloy layer magnetic thin films with different bias configuration. IEICE Transactions on Electronics E83-C (9) : 1478-1482. ScholarBank@NUS Repository.
dc.description.abstractTriple-layer CoCrPt magnetic thin films with different bias configurations were fabricated by DC magnetron sputtering on CrV and glass substrate. In-plane coercivity (Hc) showed an increase for those films with bias sputtered CoCrPt layer. The in-plane coercivity (Hc) was optimized in NB-B-NB type film prepared with substrate heating at 300°C (NB: no bias and B: rf bias applied in sputtering). Better in-plane crystal texture was observed in NB-B-NB type film by XRD and this is believed to be the main reason for the coercivity improvement. The other resource for the coercivity improvement was due to the decoupling of intergrain magnetic interactions. This was discussed accordingly to the results obtained from TEM, MFM and SIMS depth profiling.
dc.contributor.departmentMATERIALS SCIENCE
dc.description.sourcetitleIEICE Transactions on Electronics
Appears in Collections:Staff Publications

Show simple item record
Files in This Item:
There are no files associated with this item.

Google ScholarTM


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.