Title: Embrittlement of brazed martensitic stainless steel
Authors: Goh, G.K.L. 
Lim, L.C. 
Issue Date: Mar-1998
Citation: Goh, G.K.L.,Lim, L.C. (1998-03). Embrittlement of brazed martensitic stainless steel. Materials Science and Technology 14 (3) : 251-256. ScholarBank@NUS Repository.
Abstract: Brazing of AISI 410 martensitic stainless steel (12%Cr) with boron containing nickel based filler metal was observed to lead to two major embrittlement effects - temper embrittlement and brazement embrittlement. Temper embrittlement, resulting from slow cooling of the material after brazing, affects both the dimple rupture and final brittle fracture portions of the impact energy of the material. Brazement embrittlement, resulting largely from the fine intra- and intergranular boride precipitates in the base metal adjacent to the braze, significantly limits the extent of dimple rupture before the onset of brittle fracture of the material under impact conditions. A simple analysis is presented which shows that the dimple rupture portion E d and the brittle fracture portion E b of the impact energy are affected differently by the above embrittlement mechanisms. Their order of significance is as follows: ΔE″ d > ΔE′ d > ΔE′ b, where the double prime and single prime indicate the energy associated with brazement and temper embrittlement, respectively. When both embrittlement effects occur simultaneously, brazement embrittlement has a greater effect than temper embrittlement in ΔE d estimation. © 1998 The Institute of Materials.
Source Title: Materials Science and Technology
URI: http://scholarbank.nus.edu.sg/handle/10635/92695
ISSN: 02670836
Appears in Collections:Staff Publications

Show full item record
Files in This Item:
There are no files associated with this item.

Page view(s)

41
checked on Oct 19, 2018

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.