Title: Glass forming ability of La-rich La-Al-Cu ternary alloys
Authors: Tan, H. 
Lu, Z. 
Yao, H.
Yao, B. 
Feng, Y. 
Li, Y. 
Keywords: Differential thermal analysis
Eutectic composition
Glass forming ability
Lanthanum-rich lanthanum-aluminium-copper alloys
Melting behavior
Reduced glass transition temperature
Issue Date: 2001
Source: Tan, H.,Lu, Z.,Yao, H.,Yao, B.,Feng, Y.,Li, Y. (2001). Glass forming ability of La-rich La-Al-Cu ternary alloys. Materials Transactions 42 (4) : 551-555. ScholarBank@NUS Repository.
Abstract: Melting behavior and the reduced glass transition temperature (Trg) in La-rich La-Cu-Al based alloys was systematically investigated. It was found that reduced glass transition temperature increased to the maximum when the liquidus temperature decreased to the minimum for La86-xCuxAl14 (x = 10-36) alloys. The best glass formation in La-rich La-Cu-Al ternary system was obtained at La66Cu20Al14 alloy, which is at a eutectic point with the highest reduced glass transition temperature of 0.541 among these alloys. The glass forming ability of these alloys is correlated and discussed with their reduced glass transition temperature.
Source Title: Materials Transactions
URI: http://scholarbank.nus.edu.sg/handle/10635/91493
ISSN: 13459678
Appears in Collections:Staff Publications

Show full item record
Files in This Item:
There are no files associated with this item.

Page view(s)

32
checked on Feb 24, 2018

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.