Please use this identifier to cite or link to this item:
|Title:||Highly chemical ordered L11 CoPt (111) films with perpendicular anisotropy grown on glass substrates|
|Citation:||Yang, Y., Chen, J.S., Chow, G.M. (2011-04-01). Highly chemical ordered L11 CoPt (111) films with perpendicular anisotropy grown on glass substrates. Journal of Applied Physics 109 (7) : -. ScholarBank@NUS Repository. https://doi.org/10.1063/1.3561115|
|Abstract:||In this study, L11 CoPt (111) films were deposited on glass substrates at 300°C with observed superlattice (111) and (333) peaks and easy axis distribution of 2°. The magnetic anisotropy constant was in the order of 107 erg/cm3. The effect of CoPt layer thickness on domain structure and magnetic properties was investigated. With increasing film thickness, the squareness was reduced and the nucleation field changed from negative to positive, indicating low impedance to domain wall motion and increased demagnetizing energy. Magnetic force microscopy images demonstrated the magnetic domain structure changed from irregular and large domains to highly interconnected stripes with increasing CoPt layer thickness. © 2011 American Institute of Physics.|
|Source Title:||Journal of Applied Physics|
|Appears in Collections:||Staff Publications|
Show full item record
Files in This Item:
There are no files associated with this item.
checked on Jul 18, 2018
WEB OF SCIENCETM
checked on Jun 4, 2018
checked on Mar 12, 2018
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.