Title: | Low temperature deposited L 10 FePt-C (001) films with high coercivity and small grain size | Authors: | Chen, J.S. Lim, B.C. Hu, J.F. Liu, B. Chow, G.M. Ju, G. |
Issue Date: | 2007 | Citation: | Chen, J.S., Lim, B.C., Hu, J.F., Liu, B., Chow, G.M., Ju, G. (2007). Low temperature deposited L 10 FePt-C (001) films with high coercivity and small grain size. Applied Physics Letters 91 (13) : -. ScholarBank@NUS Repository. | Abstract: | FePt-C films with high coercivity, (001) texture, and small grain size were deposited on MgOCrRu /glass substrate by cosputtering FePt and carbon at 350 °C. The out-of-plane coercivity measured at room temperature increased from 9.6 to 15.1 kOe when C concentrations increased from 0% to 15%. Further increasing the C contents to 20% and 25% caused the decrease of coercivity to 13.6 and 11.8 kOe, respectively. With C doping, a two-layer structure of FePt-C films was formed and fcc-phase FePt particles were found. By optimizing the sputtering process, FePt-C (001) film with coercivity higher than 14.4 kOe and columnar FePt grains of 7.5 nm in diameter was obtained, which are suitable for ultrahigh density perpendicular recording. © 2007 American Institute of Physics. | Source Title: | Applied Physics Letters | URI: | http://scholarbank.nus.edu.sg/handle/10635/86501 | ISSN: | 00036951 |
Appears in Collections: | Staff Publications |
Show full item record
Files in This Item:
There are no files associated with this item.
Google ScholarTM
Check
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.