|Title:||Grain isolated L 10 FePt- Ta2 O5 nanocomposite films with large coercivity for perpendicular recording applications|
|Source:||Lim, B.C., Chen, J.S., Hu, J.F., Lwin, P.W., Ding, Y.F., Cher, K.M., Liu, B. (2009). Grain isolated L 10 FePt- Ta2 O5 nanocomposite films with large coercivity for perpendicular recording applications. Journal of Applied Physics 105 (7) : -. ScholarBank@NUS Repository. https://doi.org/10.1063/1.3074133|
|Abstract:||L 10 FePt- Ta2 O5 films with (001) texture were synthesized by cosputtering FePt and Ta2 O5 targets and in situ heated at 350 °C. The (001) preferred orientation was preserved even when doped with 20 vol % Ta2 O5. The out-of-plane coercivity, Hc, increased from 6.7 kOe (for pure FePt film) to 8.8 kOe when doped with 20 vol % Ta2 O5. Further increase in the dopant content to 25 and 30 vol % caused Hc to decrease significantly to below 3 kOe. Well-isolated FePt grains of tall column structures were observed for the 12 nm thick FePt film when doped with 20 vol %. The loop slope parameter, α, of such FePt film approached 1. © 2009 American Institute of Physics.|
|Source Title:||Journal of Applied Physics|
|Appears in Collections:||Staff Publications|
Show full item record
Files in This Item:
There are no files associated with this item.
checked on Feb 21, 2018
WEB OF SCIENCETM
checked on Jan 16, 2018
checked on Feb 18, 2018
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.