|Title:||Glass formation and microstructure evolution in Al-Ni-RE (RE = La, Ce, Pr, Nd and misch metal) ternary systems|
|Source:||Yang, H., Wang, J.Q., Li, Y. (2007-09). Glass formation and microstructure evolution in Al-Ni-RE (RE = La, Ce, Pr, Nd and misch metal) ternary systems. Philosophical Magazine 87 (27) : 4211-4228. ScholarBank@NUS Repository. https://doi.org/10.1080/14786430701537961|
|Abstract:||Glass formation has been systematically studied in melt-spun Al-rich Al-Ni-RE (RE = La, Ce, Pr, Nd and Mm; Mm = misch metal) alloys by navigating the compositions following the observation of microstructure evolution in the resulting ribbons. The optimum glass-forming regions are similarly located around Al85Ni10RE5 and found in the centre of the composites with primary phase -Al, Al11RE3 and Al3Ni. The similarities in the critical cross-section below which a component is fully amorphous and the optimum compositions in these Al-Ni-RE systems are interpreted in terms of their competing crystalline phases and thermodynamic properties. Interestingly, it is indicated that Ni content is markedly higher than RE content in the best glass-forming alloys, which may be associated with strong interaction between Ni-Al atom pairs and the dense packing due to Ni-centred clusters.|
|Source Title:||Philosophical Magazine|
|Appears in Collections:||Staff Publications|
Show full item record
Files in This Item:
There are no files associated with this item.
checked on Feb 28, 2018
WEB OF SCIENCETM
checked on Feb 20, 2018
checked on Mar 12, 2018
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.