Title: Observations and analyses on the thermal stability of (1 - X)Pb(Zn 1/3Nb2/3)O3-xPbTiO3 thin films
Authors: Yu, S.
Yao, K.
Tay, F.E.H. 
Issue Date: 21-Aug-2007
Citation: Yu, S., Yao, K., Tay, F.E.H. (2007-08-21). Observations and analyses on the thermal stability of (1 - X)Pb(Zn 1/3Nb2/3)O3-xPbTiO3 thin films. Chemistry of Materials 19 (17) : 4373-4377. ScholarBank@NUS Repository. https://doi.org/10.1021/cm071027l
Abstract: Relaxor ferroelectric (1 - x)Pb(Zn1/3Nb2/3)O 3-xPbTiO3 ((1 - x)PZN-xPT) thin films with x = 0.1-0.6 were prepared on (001)-oriented single-crystal LaAlO3 (LAO) substrates using a polyethylene glycol) (PEG)-modified sol-gel method. The films of the different compositions were annealed at different temperatures with varied duration. The evolution of the crystalline structure of the films with different heating conditions was analyzed using X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and micro-Raman spectra. Our experimental results showed that the thermal stability of the (1 - x)PZN-xPT perovskite phase degraded with reducing the PT amount and increasing annealing temperature and duration. A bond valence method for analyzing perovskite structural stability was developed with corrected bond lengths at the high annealing temperature. The observed thermal stability of the perovskite phase in the (1 - x)PZN-xPT system could be well explained accordingly. © 2007 American Chemical Society.
Source Title: Chemistry of Materials
URI: http://scholarbank.nus.edu.sg/handle/10635/85510
ISSN: 08974756
DOI: 10.1021/cm071027l
Appears in Collections:Staff Publications

Show full item record
Files in This Item:
There are no files associated with this item.

SCOPUSTM   
Citations

4
checked on Jul 21, 2018

WEB OF SCIENCETM
Citations

4
checked on Jun 6, 2018

Page view(s)

31
checked on Apr 20, 2018

Google ScholarTM

Check

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.