|Title:||Functional properties of electrospun NiO/RuO 2 composite carbon nanofibers|
|Citation:||Wu, Y., Balakrishna, R., Reddy, M.V., Nair, A.S., Chowdari, B.V.R., Ramakrishna, S. (2012-03-15). Functional properties of electrospun NiO/RuO 2 composite carbon nanofibers. Journal of Alloys and Compounds 517 : 69-74. ScholarBank@NUS Repository. https://doi.org/10.1016/j.jallcom.2011.12.019|
|Abstract:||One-dimensional (1D) nickel oxide/ruthenium oxide (NiO/RuO 2)-carbon composite nanofibers (NiRu-C-NFs) were fabricated via electrospinning of a homogenous mixture of polyacrylonitrile (PAN) and Ni/Ru salt precursors at different ratios followed by heat treatments. The 1D nanostructures of the composite material were characterized by field-emission scanning electron microscopy (FE-SEM), powder X-ray diffraction (XRD), Rietveld refinement and Brunauer-Emmett-Teller (BET) surface area measurements. Li-cycling properties were evaluated using cyclic voltammetry and galvanostatic properties. The asymmetric hybrid supercapacitor studies were carried out with activated carbon as a cathode and NiRu-C-NFs composites as anodes in the cycling range, 0.005-3.0 V using 1 M LiPF 6 (EC;DMC) electrolyte. NiRu-C-NFs fabricated from 5 wt% nickel (II) and 15 wt% ruthenium (III) precursors showed a capacitance up to ∼60 F g -1 after 30 cycles. Anodic Li-cycling studies of NiRu-C-NF-0 and NiRu-C-NF-2 composite samples showed a reversible capacity of 230 and 350 m Ahg -1 at current rate of 72 mA g -1 at the end of 40th cycle in the voltage range of 0.005-3.0 V. Electrochemical impedance studies (EIS) on NiRu-C-NFs showed lower impedance value for 15 wt% Ru than the bare sample. © 2011 Elsevier B.V.|
|Source Title:||Journal of Alloys and Compounds|
|Appears in Collections:||Staff Publications|
Show full item record
Files in This Item:
There are no files associated with this item.
checked on Jul 14, 2018
WEB OF SCIENCETM
checked on Jun 20, 2018
checked on May 18, 2018
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.