Title: Enhancing the stability of polymer solar cells by improving the conductivity of the nanostructured MoO3 hole-transport layer
Authors: Elumalai, N.K.
Saha, A.
Vijila, C.
Jose, R.
Jie, Z.
Ramakrishna, S. 
Issue Date: 14-May-2013
Citation: Elumalai, N.K., Saha, A., Vijila, C., Jose, R., Jie, Z., Ramakrishna, S. (2013-05-14). Enhancing the stability of polymer solar cells by improving the conductivity of the nanostructured MoO3 hole-transport layer. Physical Chemistry Chemical Physics 15 (18) : 6831-6841. ScholarBank@NUS Repository. https://doi.org/10.1039/c3cp50994j
Abstract: This article demonstrates improvements in the operational stability of organic solar cells (OSCs) by taking advantage of the relationship between oxygen stoichiometry and conductivity in nanostructured metal oxide semiconductors (n-MOS). OSCs in the inverted device configuration of ITO/Ca/P3HT:PCBM/MoO3/Ag were employed in the present study. A high degree of oxygen defects were introduced in the hole-conducting MoO3 layer by annealing the devices under vacuum (≥10-5 mbar) for nominal temperature (120 °C) and time (10 min). The above devices had much higher operational stability, when tested following the ISOS-D-1 (shelf) protocol, than control devices annealed conventionally, i.e., in nitrogen atmosphere. Employing current-voltage measurement as functions of temperature and photon flux, we show that the devices annealed under vacuum have a lesser density of traps than those annealed in nitrogen. The lesser trap density is shown to be beneficial in reducing the rate of electron recombination thereby increasing the operational stability of the corresponding device. A number of experiments were undertaken to show that the difference in the operation stability of the device results from the difference in conductivity of the nanostructured MoO3 hole transporting layer. The charge extraction by linear increasing voltage spectroscopy shows that charges are relaxed at the trap states in the device annealed in nitrogen whereas they are efficiently transported in the other device. We identify that building up of an interfacial potential barrier as a result of the charge relaxation at the trap states and the corresponding chemical changes in the devices annealed conventionally is the source of degradation of the device performance over time. To our knowledge, this is the first report that successfully overcomes hole-conductivity induced degradation in organic solar cells. © 2013 the Owner Societies.
Source Title: Physical Chemistry Chemical Physics
URI: http://scholarbank.nus.edu.sg/handle/10635/85159
ISSN: 14639076
DOI: 10.1039/c3cp50994j
Appears in Collections:Staff Publications

Show full item record
Files in This Item:
There are no files associated with this item.

SCOPUSTM   
Citations

32
checked on Oct 22, 2018

WEB OF SCIENCETM
Citations

23
checked on Nov 22, 2017

Page view(s)

31
checked on Sep 28, 2018

Google ScholarTM

Check

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.