Title: Effects of heat treatment and magnetoannealing on nanocrystalline Co-ferrite powders
Authors: Wang, Y.C.
Ding, J. 
Yin, J.H.
Liu, B.H. 
Yi, J.B. 
Yu, S. 
Issue Date: 2005
Source: Wang, Y.C., Ding, J., Yin, J.H., Liu, B.H., Yi, J.B., Yu, S. (2005). Effects of heat treatment and magnetoannealing on nanocrystalline Co-ferrite powders. Journal of Applied Physics 98 (12) : -. ScholarBank@NUS Repository. https://doi.org/10.1063/1.2148632
Abstract: This work consists of three parts: the effects of heat treatment (slow cooling and quenching), magnetoannealing, and postannealing of samples with induced anisotropy. It has been found that noncomplete inverse spinel structure was the result after annealing at higher temperature and quenching. Our Mössbauer spectroscopy study confirmed noncomplete inverse structure after quenching, while inverse spinel structure was formed after slow cooling. The kinetics of the formation of induced anisotropy during magnetoannealing has been investigated in this study. Reduction of crystalline magnetic anisotropy was observed, as coercivity decreased after magnetoannealing. The change of remanence ratio and coercivity followed the expected equations for ion diffusion. A relative large anisotropy in magnetization was evident. A postannealing resulted in the conversion into the initial isotropic stage. The process could be well described using the equations of ion diffusion. © 2005 American Institute of Physics.
Source Title: Journal of Applied Physics
URI: http://scholarbank.nus.edu.sg/handle/10635/68211
ISSN: 00218979
DOI: 10.1063/1.2148632
Appears in Collections:Staff Publications

Show full item record
Files in This Item:
There are no files associated with this item.

SCOPUSTM   
Citations

19
checked on Dec 13, 2017

WEB OF SCIENCETM
Citations

16
checked on Nov 15, 2017

Page view(s)

67
checked on Dec 9, 2017

Google ScholarTM

Check

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.