|Title:||Heat-treating below recrystallization temperature to enhance compressive failure strain and work of fracture of magnesium|
|Authors:||Paramsothy, M. |
|Citation:||Paramsothy, M., Srikanth, N., Hassan, S.F., Gupta, M. (2008-10-25). Heat-treating below recrystallization temperature to enhance compressive failure strain and work of fracture of magnesium. Materials Science and Engineering A 494 (1-2) : 436-444. ScholarBank@NUS Repository. https://doi.org/10.1016/j.msea.2008.04.049|
|Abstract:||New bimetal magnesium/aluminium macrocomposite containing millimeter-scale Al core reinforcement was fabricated using solidification processing followed by hot coextrusion. Microstructural characterisation revealed increased grain size, Mg texture change and unbalanced interfacial interdiffusion of Mg and Al into each other. Stress at the bimetal interface was attributed to solid solution formation, thermal expansion mismatch, unbalanced Kirkendall strain, lattice misfit strain, and strain localization effects, these being interface localized strengthening phenomena. Compressive testing revealed that presence of Al core decreased 0.2% YS (-23%) and ultimate compressive strength (UCS) (-11%), but significantly increased failure strain (+134%) and work of fracture (+60%) of Mg in the as-extruded macrocomposite. Also, interfacial relaxation during heat treating significantly increased failure strain (+17%) and work of fracture (+17%) of Mg/Al macrocomposite without compromising 0.2% YS and UCS. The effects of presence of millimeter-scale Al core as well as interfacial relaxation on the compressive properties of the bimetal macrocomposite are investigated in this paper. © 2008 Elsevier B.V. All rights reserved.|
|Source Title:||Materials Science and Engineering A|
|Appears in Collections:||Staff Publications|
Show full item record
Files in This Item:
There are no files associated with this item.
checked on Jul 12, 2018
WEB OF SCIENCETM
checked on Jun 5, 2018
checked on May 18, 2018
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.