Title: Analysis of fatigue crack growth in a rubber-toughened epoxy resin: effect of temperature and stress ratio
Authors: Abou-Hamda, M.
Mai, Y.-W.
Wu, S.-X.
Cotterell, B. 
Keywords: Coffin-Manson law
crack closure
damage accumulation
fatigue crack propagation
fatigue models
rubber-modified epoxy
stress ratio
Issue Date: Oct-1993
Source: Abou-Hamda, M.,Mai, Y.-W.,Wu, S.-X.,Cotterell, B. (1993-10). Analysis of fatigue crack growth in a rubber-toughened epoxy resin: effect of temperature and stress ratio. Polymer 34 (20) : 4221-4229. ScholarBank@NUS Repository.
Abstract: Fatigue crack propagation in a rubber-toughened epoxy resin was studied at different test temperatures (-40 to 60°C) and stress ratios (0.05 to 0.70) using single edge-notched specimens at a frequency of 5 Hz. Fatigue crack propagation rates ( da dN) were plotted against the stress-intensity factor amplitude (ΔK) in accordance with the Paris power-law equation. For a given stress ratio da dN was not sensitive to variations in test temperature. But for a given temperature da dN increased with stress ratio. Using the Williams' two-stage line zone model to analyse these experimental data, it was shown that the main failure process was due to shear plastic flow at the crack tip. The fatigue stress and the closure stress-intensity factor both decreased with increasing temperature, implying that more severe damage had occurred at higher testing temperatures. The experimental data were also analysed in terms of a new fatigue model, which considers the accumulation of damage due to cyclic plastic strain in the reversed plastic zone similar to the Coffin-Manson law and crack closure due to residual plastic stretch at the crack wake. There was good agreement between theory and experiment, suggesting a simpler way to correlate fatigue crack growth rates in this and other polymeric materials. © 1993.
Source Title: Polymer
URI: http://scholarbank.nus.edu.sg/handle/10635/57907
ISSN: 00323861
Appears in Collections:Staff Publications

Show full item record
Files in This Item:
There are no files associated with this item.

Page view(s)

79
checked on Feb 16, 2018

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.