Title: Occlusal contact area (OCA) wear of two new composite restoratives
Authors: Yap, A.U.J. 
Keywords: Composite
Occlusal
Restoratives
Wear
Issue Date: 2002
Source: Yap, A.U.J. (2002). Occlusal contact area (OCA) wear of two new composite restoratives. Journal of Oral Rehabilitation 29 (2) : 194-200. ScholarBank@NUS Repository. https://doi.org/10.1046/j.1365-2842.2002.00814.x
Abstract: The occlusal contact area wear resistance of two new composite restoratives (Z250 and P60) was investigated and compared with two existing materials (Silux and Z100) using a reciprocal compression-sliding test apparatus. Six wear specimens were made for each material and subjected to wear testing at 20 MPa with artificial saliva as lubricant. Wear depth (μm) was measured using profilometry every 20 000 cycles up to 120 000 cycles. Results were analysed using ANOVA/Scheffe's test (P < 0.05) and Pearson's correlation. The effects of cyclic loading on wear and counter-body loss were material dependent. Silux had the lowest wear at all cyclic intervals. At 20 000 and 40 000 cycles, Silux had significantly less wear than all the other composites evaluated, and Z100 had significantly less wear than Z250 and P60. After 60 000 cycles, significant differences in wear was observed only between Silux and the other composites. Correlation between number of cycles and wear/counter-body loss, and between wear and counter-body were significant and positive. The microfilled composite Silux had significantly better OCA wear resistance than the minifilled composites Z100, Z250 and P60. © 2002 Blackwell Science Ltd.
Source Title: Journal of Oral Rehabilitation
URI: http://scholarbank.nus.edu.sg/handle/10635/46928
ISSN: 0305182X
DOI: 10.1046/j.1365-2842.2002.00814.x
Appears in Collections:Staff Publications

Show full item record
Files in This Item:
There are no files associated with this item.

SCOPUSTM   
Citations

10
checked on Dec 6, 2017

WEB OF SCIENCETM
Citations

9
checked on Nov 22, 2017

Page view(s)

79
checked on Dec 10, 2017

Google ScholarTM

Check

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.