Title: Growth mode and microstructure of Ag-doped YBa2Cu3O7-δ thin films prepared by dual beam pulsed-laser deposition
Authors: Xu, S.Y. 
Ong, C.K. 
You, L.P. 
Li, J. 
Wang, S.J. 
Issue Date: Nov-2000
Citation: Xu, S.Y., Ong, C.K., You, L.P., Li, J., Wang, S.J. (2000-11). Growth mode and microstructure of Ag-doped YBa2Cu3O7-δ thin films prepared by dual beam pulsed-laser deposition. Physica C: Superconductivity and its Applications 341-348 : IV/-. ScholarBank@NUS Repository. https://doi.org/10.1016/S0921-4534(00)01075-3
Abstract: Ag-doped c-axis YBa2Cu3O7-δ thin films were fabricated by using dual-beam pulsed-laser deposition. When a small amount of silver was doped in the film grown at 700°C, the Jc value was obviously enhanced. The temperature dependence of Jc was found proportional to (1-T/Tc0)3/2 at T close to Tc0. In the films grown at 730°C, we observed long bar-like structures with lengths in tens of μm, oriented along or at 45° to the a/b axes of the film. The bars consisted mainly a-axis YBCO grains and a mixture of polycrystalline and amorphous oxides. Defects on substrate surface and growth temperature were found dominating in formation of the bars, which could be attributed to a Ag-assisted diffusion mechanism during the deposition process.
Source Title: Physica C: Superconductivity and its Applications
URI: http://scholarbank.nus.edu.sg/handle/10635/113081
ISSN: 09214534
DOI: 10.1016/S0921-4534(00)01075-3
Appears in Collections:Staff Publications

Show full item record
Files in This Item:
There are no files associated with this item.

SCOPUSTM   
Citations

2
checked on Jul 19, 2018

WEB OF SCIENCETM
Citations

7
checked on Jul 3, 2018

Page view(s)

41
checked on Jul 6, 2018

Google ScholarTM

Check

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.