|Title:||Structure, bonding state and in-vitro study of Ca-P-Ti film deposited on Ti6A14V by RF magnetron sputtering|
In-vitro cell culturing
|Citation:||Long, J.D., Xu, S., Cai, J.W., Jiang, N., Lu, J.H., Ostrikov, K.N., Diong, C.H. (2002-05-31). Structure, bonding state and in-vitro study of Ca-P-Ti film deposited on Ti6A14V by RF magnetron sputtering. Materials Science and Engineering C 20 (1-2) : 175-180. ScholarBank@NUS Repository. https://doi.org/10.1016/S0928-4931(02)00029-2|
|Abstract:||Experimental investigation of functionally graded calcium phosphate-based bio-active films on Ti-6A1-4V orthopaedic alloy prepared in an RF magnetron sputtering plasma reactor is reported. The technique involves concurrent sputtering of Hydroxyapatite (HA) and Ti targets, which results in remarkably enhanced adhesion of the film to the substrate and stability of the interface. The films have been characterized using X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The XPS data show that the films are composed of O, Ca, P and Ti, and reveal the formation of O=P groups and hybridization of O-Ca-P. The XRD pattern shows that the Ca-P thin films are of crystalline calcium oxide phosphate (4CaO·P2O5) with preferred orientation varying with processing parameters. High-resolution optical emission spectra show that the emission of CaO is dominant. The CaO, PO and CaPO species are strongly influenced by deposition conditions. The introduction of Ti element during deposition provides a stable interface between bio-inert substrates Ti-6A1-4V and bioactive HA coating. In-vitro cell culturing tests suggest excellent biocompatibility of the Ca-P-Ti films. © 2002 Elsevier Science B.V. All rights reserved.|
|Source Title:||Materials Science and Engineering C|
|Appears in Collections:||Staff Publications|
Show full item record
Files in This Item:
There are no files associated with this item.
checked on Sep 13, 2018
WEB OF SCIENCETM
checked on Sep 5, 2018
checked on Jul 6, 2018
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.