|Title:||The effect of additive Ag layers on the L10 FePt phase transformation|
|Authors:||Zhao, Z.L. |
Magnetic recording media
|Citation:||Zhao, Z.L., Chen, J.S., Ding, J., Inaba, K., Wang, J.P. (2004-11). The effect of additive Ag layers on the L10 FePt phase transformation. Journal of Magnetism and Magnetic Materials 282 (1-3) : 105-108. ScholarBank@NUS Repository. https://doi.org/10.1016/j.jmmm.2004.04.026|
|Abstract:||The effect of ultrathin (nominal thickness of 0.25nm) Ag layers added in different locations of FePt thin film on the L10 FePt phase ordering has been investigated. After the Ag layer is deposited on the bottom of the FePt film, the coercivity increases from about 1 to 1.6kOe. When the 0.25nm Ag layer is moved from the bottom to the top of the film, the coercivity gradually increases to about 3kOe. The δM curves suggests that the exchange coupling in the FePt film was decreased when the additive Ag layer was deposited in the middle or on the top of the FePt films while it remains unchanged when Ag layer was on the bottom of the FePt layer compared with the δM curve of FePt film without Ag layers. © 2004 Elsevier B.V. All rights reserved.|
|Source Title:||Journal of Magnetism and Magnetic Materials|
|Appears in Collections:||Staff Publications|
Show full item record
Files in This Item:
There are no files associated with this item.
checked on Jan 15, 2019
WEB OF SCIENCETM
checked on Jan 7, 2019
checked on Dec 28, 2018
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.