Title: Thermal stability of the αZn-Mg2Zn11 and αZn-βAl eutectics obtained by Bridgman growth
Authors: Liu, H.Y.
Li, Y. 
Jones, H.
Issue Date: 1998
Citation: Liu, H.Y.,Li, Y.,Jones, H. (1998). Thermal stability of the αZn-Mg2Zn11 and αZn-βAl eutectics obtained by Bridgman growth. Journal of Materials Science 33 (5) : 1159-1164. ScholarBank@NUS Repository.
Abstract: The thermal stability of rod-like αZn-Mg2Zn11 and lamellar αZn-βAl eutectics obtained by Bridgman growth of Zn-3.1 wt% Mg and Zn-5 wt% Al has been studied for soaking times up to 10 h at 300 and 350°C, respectively. Two-dimensional coarsening resulted for αZn-Mg2Zn11 grown at 0.5 and 1 mm s-1 while fault migration was operative for lamellar αZn-βAl grown at 0.1 and 1 mm s-1. Hardness decreased with increased soaking time according to a Hall Petch relationship with mean interphase spacing and the values H0 and kY accord well with the values obtained from the Hall Petch relationship for HV of as-solidified αZn-Mg2Zn11 and αZn-βAl with eutectic interphase spacing, respectively. © 1998 Chapman & Hall.
Source Title: Journal of Materials Science
URI: http://scholarbank.nus.edu.sg/handle/10635/107243
ISSN: 00222461
Appears in Collections:Staff Publications

Show full item record
Files in This Item:
There are no files associated with this item.

Page view(s)

41
checked on Oct 12, 2018

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.