Title: No corrosion of 304 stainless steel implant after 40 years of service
Authors: Blackwood, D.J. 
Pereira, B.P.
Issue Date: Jul-2004
Citation: Blackwood, D.J., Pereira, B.P. (2004-07). No corrosion of 304 stainless steel implant after 40 years of service. Journal of Materials Science: Materials in Medicine 15 (7) : 755-758. ScholarBank@NUS Repository. https://doi.org/10.1023/B:JMSM.0000032814.20695.3c
Abstract: When exposed to 0.9% NaCl type 304 stainless steel undergoes severe pitting corrosion within a matter of days. However, a Sherman plate fabricated from type 304 stainless steel remained inside a patient's arm for almost 40 years without any visible indications of corrosion. Given the previous understanding of the pathological environments this was considered quite remarkable. It is proposed that the low dissolved oxygen levels found in human-body fluids makes the long-term in vivo environment much more benign than would be anticipated from in vitro experiments. Furthermore, it is proposed that previous cases of localized pitting corrosion on stainless steel implants most likely arose due to the development of short-term aggressive conditions due to pathological changes in the surrounding tissue as a result of the trauma of the implant procedure. In the present case the Sherman plate was sufficiently small that the surrounding tissue was not aggravated sufficiently to lead to the development of such an environment aggressive. The conclusion that surgical implants are at most risk during the first few weeks of service implies that short-term corrosion protection methods, such as coatings, may be more effective than previously thought.
Source Title: Journal of Materials Science: Materials in Medicine
URI: http://scholarbank.nus.edu.sg/handle/10635/107143
ISSN: 09574530
DOI: 10.1023/B:JMSM.0000032814.20695.3c
Appears in Collections:Staff Publications

Show full item record
Files in This Item:
There are no files associated with this item.

SCOPUSTM   
Citations

8
checked on Aug 14, 2018

WEB OF SCIENCETM
Citations

8
checked on Aug 14, 2018

Page view(s)

27
checked on Jul 13, 2018

Google ScholarTM

Check

Altmetric


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.